Hollow Bars Ni Hard Liners Wear Resistant Plates Ni hard 4
Ni-hard4 Wear-resistant Plates Made in China
1. Our materials conform to
ASTM A 532 1-A, B, C, D,
ASTM A 532 2-A, B, C, D, E,
ASTM A 532 3-A.
2. International Standard: AS 2027-2002/Ni hard 4.
3. The hardness of Ni-hard castings is more than HRC56.
4. Specific weight or density: 7.3~7.5g/mm2.
5. Microstructure: Eutectic Carbide + Martensite + Residual
6. Break Point: 25~40kg/mm2.
The Combined Self-fastened Boltless Ball Mill Liners
The outstanding advantage of our liners is boltless.
The general advantages in ball mills are as follows:
Power Consumption Reduced
The liners are easily installed and existing mills need no
The additional advantages in cement mills are as follows:
No leakage of slurry
No repairs during service periods
Better reliability and stability
In the recent 20 years, our liners have been widely used in large,
medium and small ball mills in
Chinese power generation, mining,cement, chemical engineering and metallurgical industries and
super fine pulverizing equipments. It is the only recommended liner product in the latest standard
of the electric-power industry in China.
Materials 1: Double-Media Quenching Chromium-Molybdenum Alloy Steel
We specially design the material for ball mill liners in mines,
coalfired power plants and cement plants,
etc.. With our special doublemedia quenching process, the material can
not only achieve ideal hardness
(HRC48~55) but also ideal toughness value (AK30~100J). It can
completely meet the requirement of
linersof large and middlesize ball mills at home and abroad. The match of
Middle Chrome Liners and
Cast Balls has been the typical model in coal mills and cement
mills. Meanwhile, the material is
applicable to the teeth plates, armored plates and hammers of crushers and excavator
Materials 2: Pearlitic Chromium-Molybdenum Alloy Steel Series
The Pearlitic Chromium-Molybdenum Alloy Steel Liners are widely
used in AG Mill,SAG Mill and Ball
Hardness: HB310-375 (equivalent to HRC33-42)
Impact resistant Value: Ak≥60J (60×10×10mm) in normal ambient
We can produce pearlitic Cr-Mo steel as per AS2074 Gr. L / 2B.
Materials 3 : High Chrome White Iron Series
High Chrome white iron we can produce include 15%Cr, 18%Cr, 20%Cr
and 26Cr. Under same working
condition,the wear performance of High Chrome mill liners is four times of
that of high manganese steel
liners and twice of that of low Chrome alloy steel liners.Meanwhile, we can produce high Chrome
as per AS2027, ASTM A532 and BS4844.Customer-made Mill Liners
In addition to our patented Boltless Mill Liners, we can produce
liners as per the request of customers.
So far, we have been the regular suppliers of mill liners for
Magotteaux and Foster Wheeler Power Group.
Now, we have supplied steel caps inserted in rubber lifters for SAG
mills and AG mills to some mines in Australia and New Zealand. Wear Parts for CrusherJaw plates and cheek plates for jaw crushers, blow bars and impact
plates for impact crushers, cone liners forgy ratory crushers, hammers for hammer crushers and concaves and
mantles for cone crushers.
Depending on the specific working conditions, all wear parts can be
ordered as Manganese Steel, high Cr cast iron or Cr-Mo Alloy Steel.
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant
Alloy Steel I
Alloy Steel II
Alloy Steel III
High Cr white iron
High Cr Alloy Steel
High Manganese Steel
Ni-Hard cast iron
AS 2074 L2B Mod
AS 2027 Cr27
AS 2027 CrMo 15/3
AS 2027 CrMo 20/2/1
ASTM A532 Class III type A 25% Cr
ASTM A532Class II type B 15% Cr-Mo
BS 4844 3E
JIS G 5153-1999
ASTM A 128
ASTM A 532 1-A,B,C,D
ASTM A 532 2-A,B,C,D,E
ASTM A 532 3-A
Pearlitic Cr Mo Steel
Austenitic Mn Steel
This product, invented by Mr. Chen Changshun, senior engineer and
the director of the company, is known as “China Best Liner”.
It includes two parts, high wear resistance boltless plates, and
highly expandable riveting plates,
which are self-fastened and strengthened to withstand impact from mill balls.
We possess famous patented product------
Combined Self-fastened (Boltless) Ball Mill Liners, or Called CHINA
In 2012, we registered a new patent about Liner Technology.
In December of 2000, we successfully registered the international
patent in Canada.
In 1988 and 1997, we claimed domestic patents for ball mill liners